B65A470硅钢片 高导磁低铁损

电工钢硅钢片Electrical steel, also known as silicon steel sheet, is an indispensable metal material in the power, electronics, and military industries, and is also the largest functional material in production. It is mainly used as the iron core for various motors, generators, and transformers. Since it is a functional material, its performance testing also revolves around "function". These indicators are often mentioned in trade and processing processes, and a brief understanding can help everyone better carry out their work. The performance testing of electrical steel mainly includes the following aspects: magnetic inspection, stacking coefficient inspection, coating adhesion inspection, repeated bending inspection, size and shape surface inspection, and conventional mechanical property inspection. In addition to the types of products listed above, there are also some special purpose electrical steel plates, such as 0.15 and 0.20mm thick 3％ Si cold-rolled non oriented silicon steel strips and 0.025, 0.05, and 0.1mm thick 3％ Si cold-rolled oriented silicon steel strips, which are used as intermediate and intermediate grade High frequency motors and transformers, as well as pulse transformers, etc； 0.7mm thick 3％ Si high-strength cold-rolled non oriented silicon steel plate for relays and power switches； High strength cold-rolled electrical steel plate for new high-speed motor rotors； Low carbon electrical steel hot-rolled thick and cold-rolled plates for magnetic shielding and high-energy accelerator electromagnets such as medical magnetic resonance tomography scanners； 4.5％ to 6.5％ Si high silicon steel plates for high-frequency motors, transformers, and magnetic shielding. Generally, motors, transformers, and other electrical components are required to have high efficiency, low power consumption, small size, and light weight. Electrical steel plates are usually guaranteed to have magnetic properties based on core loss and magnetic induction strength. Magnetic induction strength is the number of magnetic lines passing through a unit cross-sectional area of the iron core, also known as magnetic flux density. It represents the material‘s magnetization ability, measured in T. The magnetic induction strength of electrical steel plates is high, and the excitation current (also known as no-load current) of the iron core is reduced. Copper and iron losses are also reduced, which can save electrical energy. When the power of the motor and transformer remains constant, the magnetic induction intensity is high, and the design Bm can be increased. The cross-sectional area of the iron core can be reduced, which reduces the volume and weight of the iron core, and saves the amount of electrical steel plates, wires, insulation materials, and structural materials used. This can reduce the total loss and manufacturing cost of the motor and transformer, and is beneficial for the manufacturing, installation, and transportation of large transformers and motors. The main requirements for the performance of silicon steel are: 1. Low iron loss is the most important indicator of the quality of silicon steel sheets. Various countries classify grades based on iron loss values, with the lower the iron loss, the higher the grade. 2. Under strong magnetic fields, the magnetic induction intensity (magnetic induction) is high, which reduces the volume and weight of the iron core of the motor and transformer, saving silicon steel sheets, copper wires, and insulation materials. 3. The surface is smooth, flat, and the thickness is uniform, which can improve the filling coefficient of the iron core. 4. Good lamination performance is more important for manufacturing micro and small electric motors. 5. The adhesion and weldability of the surface insulation film are good, which can prevent corrosion and improve the punching performan

电工钢硅钢片自粘接涂层Z C3 C-3 - C-3涂层为有机成分，具有很高的层间电阻，并可以大幅提高钢带的冲片性能，很适合用于冲压叠片。用户使用时，先将钢板冲制成铁心叠片，然后加压固定成型，在保压条件下加热固化，叠片彼此粘接在一起，形成整体。其固定方式和常见的铆接、辽宁抚顺同城焊接、辽宁抚顺同城螺栓方式不同，刚度、辽宁抚顺同城强度更高，振动和噪音小。涂层交货状态为 B 状态，即涂层还没有发生完全固化，具有进一步粘接、辽宁抚顺同城固化的活性，涂层硬度、辽宁抚顺同城耐蚀性尚没有达到 。涂层钢卷仓储有效期为半年。用户固化的工艺为：a）炉烘温度 160～230℃，模具压紧的压力为 0.3～3Mpa，时间保持1～3h；或 b）感应固化的铁心温度 150~250℃，压力 0.1~3MPa，时间保持 0.2~30min。固化后，涂层处于终稳定的状态，即 C 状态，涂层硬度、辽宁抚顺同城强度、辽宁抚顺同城粘接力达到 。涂层不能承受正常的应力退火温度。涂层能承受 180℃的长期耐热温度；但考虑到粘结能力的稳定性，适用于该涂层的工作温度通常不超过 150℃。