新能源电工钢 B30AV1500解决方案

电工钢硅钢片Electrical steel, also known as silicon steel sheet, is an indispensable metal material in the power, electronics, and military industries, and is also the largest functional material in production. It is mainly used as the iron core for various motors, generators, and transformers. Since it is a functional material, its performance testing also revolves around "function". These indicators are often mentioned in trade and processing processes, and a brief understanding can help everyone better carry out their work. The performance testing of electrical steel mainly includes the following aspects: magnetic inspection, stacking coefficient inspection, coating adhesion inspection, repeated bending inspection, size and shape surface inspection, and conventional mechanical property inspection. In addition to the types of products listed above, there are also some special purpose electrical steel plates, such as 0.15 and 0.20mm thick 3％ Si cold-rolled non oriented silicon steel strips and 0.025, 0.05, and 0.1mm thick 3％ Si cold-rolled oriented silicon steel strips, which are used as intermediate and intermediate grade High frequency motors and transformers, as well as pulse transformers, etc； 0.7mm thick 3％ Si high-strength cold-rolled non oriented silicon steel plate for relays and power switches； High strength cold-rolled electrical steel plate for new high-speed motor rotors； Low carbon electrical steel hot-rolled thick and cold-rolled plates for magnetic shielding and high-energy accelerator electromagnets such as medical magnetic resonance tomography scanners； 4.5％ to 6.5％ Si high silicon steel plates for high-frequency motors, transformers, and magnetic shielding. Generally, motors, transformers, and other electrical components are required to have high efficiency, low power consumption, small size, and light weight. Electrical steel plates are usually guaranteed to have magnetic properties based on core loss and magnetic induction strength. Magnetic induction strength is the number of magnetic lines passing through a unit cross-sectional area of the iron core, also known as magnetic flux density. It represents the material‘s magnetization ability, measured in T. The magnetic induction strength of electrical steel plates is high, and the excitation current (also known as no-load current) of the iron core is reduced. Copper and iron losses are also reduced, which can save electrical energy. When the power of the motor and transformer remains constant, the magnetic induction intensity is high, and the design Bm can be increased. The cross-sectional area of the iron core can be reduced, which reduces the volume and weight of the iron core, and saves the amount of electrical steel plates, wires, insulation materials, and structural materials used. This can reduce the total loss and manufacturing cost of the motor and transformer, and is beneficial for the manufacturing, installation, and transportation of large transformers and motors. The main requirements for the performance of silicon steel are: 1. Low iron loss is the most important indicator of the quality of silicon steel sheets. Various countries classify grades based on iron loss values, with the lower the iron loss, the higher the grade. 2. Under strong magnetic fields, the magnetic induction intensity (magnetic induction) is high, which reduces the volume and weight of the iron core of the motor and transformer, saving silicon steel sheets, copper wires, and insulation materials. 3. The surface is smooth, flat, and the thickness is uniform, which can improve the filling coefficient of the iron core. 4. Good lamination performance is more important for manufacturing micro and small electric motors. 5. The adhesion and weldability of the surface insulation film are good, which can prevent corrosion and improve the punching performan

电工钢硅钢片：同一产品在磁极化强度 1.5T、河南周口同城频率 50Hz 或 60Hz 条件下，按 GB/T 13789 单片法所测得的比总损耗值，参照 GB/T 13789-2008 附录 C 中指定的关系式 C.2a 向方圈法数据转换，两种检测方法所得比总损耗转换因子δP 的拟合关系可参照 GB/T 13789-2008 附录 C 关系式 C.3a，式中拟合有效区间为1.0T～1.8T，且该转换关系只适用于 0.23mm 及以上厚度规格激光刻痕产品，0.20mm 及以下厚度规格激光刻痕产品的转换关系根据实际检测、河南周口同城应用对比实验结果进行专项规定。当供应商和用户协商对 P1.5/50 和 P1.5/60有明确要求时，转换后的 P1.5/50和 P1.5/60应符合表 3、河南周口同城表 4、河南周口同城表 5、河南周口同城表 6、河南周口同城表 7、河南周口同城表 8 和表 9 的规定。7.1.7 其他测试条件下，转换系数 Fc 可由供应商和用户协商确定。7.1.8 当需要提供磁化曲线时，按 GB/T 13789 单片法所测得数据参照 GB/T 13789-2008 附录 C 关系式转换。注1：多年来习惯上采用磁感应强度，实际上爱泼斯坦方圈和单片测试仪测量的是磁极化强度。 磁感应强度与磁极化强度的关系：J＝B-μ0H ，H＝800A/m条件下，B和J的差异约为0.001T

电工钢硅钢片本文件适用于宝山钢铁股份有限公司生产的、河南周口同城用于频率在 100Hz-10000Hz 磁路结构的、河南周口同城以终退火状态交货的全工艺冷轧无取向电工钢带产品(以下简称产品)，比总损耗(铁损)specific total loss (iron loss)比总损耗是指在磁极化波形保持正弦，其峰值和频率为特定值时，单位质量材料所消耗的总功率，比总损耗用符号 P(Jm/f)表示，单位为 W/kg。例：P1.0/400表示在 磁极化强度为 1.0T、河南周口同城频率为 400Hz 时的比总损耗。Q/BQB 481－202123.2 磁极化强度 magnetic polarization磁极化强度是指试样受交变磁化时，特定磁场强度峰值的磁极化强度峰值，其符号为J(H)，单位为 T(特斯拉)。例：J5000表示对应于磁场强度峰值为 5000A/m 下的磁极化强度峰值。4 分类本文件的材料的等级是根据磁极化强度在1.0T、河南周口同城频率在400Hz下的 比总损耗值P1.0/400、河南周口同城材料公称厚度进行牌号分类，并按产品特性细分为普通型、河南周口同城型、河南周口同城高强度型、河南周口同城高磁感型和高强度型五类。示例 1：B20AV1300 表示公称厚度为 0.20mm 的普通型无取向电工钢， 比总损耗P1.0/400为13W/kg；示例 2：B27AHV1400 表示公称厚度为 0.27mm 的型无取向电工钢， 比总损耗P1.0/400为14W/kg；示例 3：B30APV1500 表示公称厚度为 0.30mm 的高磁感型无取向电工钢， 比总损耗P1.0/400为15W/kg；示例 4：B25AHV1300M表示公称厚度为0.25mm的高强度型无取向电工钢， 比总损耗P1.0/400为13W/kg；示例 5：B35AHS500 表示公称厚度为 0.35mm 的高强度型无取向电工钢，小屈服强度500MPa。1 绝缘涂层状态产品通常以两面涂敷绝缘涂层状态交货，涂层种类见表 2。绝缘涂层应可耐受绝缘漆、河南周口同城变压器油、河南周口同城机械油等介质的侵蚀。本文件规定的绝缘涂层与国内外相关技术规范规定绝缘涂层的近似对照可参见附录 A(资料性附录)，绝缘涂层的特性见附录 B(资料性附录)。绝缘涂层的厚度、河南周口同城自粘接涂层的剥离强度等技术要求如有特殊要求应在订货时协商，并在合同中注明。涂层绝缘电阻涂层绝缘电阻分为表面绝缘电阻和层间电阻，表面绝缘电阻单位为Ω·cm2/面，层间电阻单位为Ω·cm2/片，理论上，层间电阻是表面绝缘电阻的 2 倍。根据需方要求，经供需双方协商，可进行涂层绝缘电阻的检测，并在合同中注明涂层表面绝缘电阻或层间电阻的小值。